Stabilita optického monitoru při depozici 42-vrstvého interferenčního „bandpass“ filtru 520-590 nm
Žídek, Karel
2018 - český
V této zprávě popisujeme stabilitu depozice komplikovaných soustav tenkých vrstev, které byly navrženy jako interferenční filtr s pásmovou propustností. Jde o 42 vrstev TiO2 a SiO2, které jsou monitorovány jednak tzv. krystalovým a optickým monitorem tloušťky. Diskutujeme případ, kdy je návrh IF průběžně upravován podle reálné tloušťky deponovaných vrstev. We report on stability of a deposition process of a complex system of thin layers. The layers were designed as a 42-layer bandpass interference filter. The layers of TiO2 and SiO2 were monitored both by the means of a crystal and an optical thickness monitor. We discuss the case when the design of the interference filter is continuously adapted according to the real thickness of the already deposited layers. Klíčová slova: thin layer deposition; thickness monitor; interference filter; deposition stability Plné texty jsou dostupné na jednotlivých ústavech Akademie věd ČR.
Stabilita optického monitoru při depozici 42-vrstvého interferenčního „bandpass“ filtru 520-590 nm

V této zprávě popisujeme stabilitu depozice komplikovaných soustav tenkých vrstev, které byly navrženy jako interferenční filtr s pásmovou propustností. Jde o 42 vrstev TiO2 a SiO2, které jsou ...

Žídek, Karel
Ústav fyziky plazmatu, 2018

OLGA – efficient full wave code for the coupling of LH grills
Preinhaelter, Josef; Hillairet, J.; Urban, Jakub
2018 - anglický
The full wave code OLGA, for determining the coupling of a single row lower hybrid launcher (waveguide grills) to the plasma, is extended to handle multirow multijunction active passive structures (like the C3 and C4 launchers on TORE SUPRA) by implementing the scattering matrix formalism. The extended code is still computationally fast because of the use of (i) 2D splines of the plasma surface admittance in the accessibility region of the k-space, (ii) high order Gaussian quadrature rules for the integration of the coupling elements and (iii) utilizing the symmetries of the coupling elements in the multiperiodic structures. The extended OLGA code is benchmarked against the ALOHA-1D, ALOHA-2D and TOPLHA codes for the coupling of the C3 and C4 TORE SUPRA launchers for several plasma configurations derived from reflectometry and interferometery. Unlike nearly all codes (except the ALOHA-1D code), OLGA does not require large computational resources and can be used for everyday usage in planning experimental runs. In particular, it is shown that the OLGA code correctly handles the coupling of the C3 and C4 launchers over a very wide range of plasma densities in front of the grill. Klíčová slova: lower hybrid waves; coupling; large multirow multijunction grills; tokamak; full-wave Dokument je dostupný na externích webových stránkách.
OLGA – efficient full wave code for the coupling of LH grills

The full wave code OLGA, for determining the coupling of a single row lower hybrid launcher (waveguide grills) to the plasma, is extended to handle multirow multijunction active passive structures ...

Preinhaelter, Josef; Hillairet, J.; Urban, Jakub
Ústav fyziky plazmatu, 2018

Dalekohledy typu Dall-Kirkham
Rail, Zdeněk; Ulrichová, Iva; Kuryshev, V.; Vápenka, David
2018 - český
Referát se zabývá optickými vadami dvojzrcadlových dalekohledů s elipsoidálními primárními a sférickými sekundárními zrcadly. Systém byl objeven na konci dvacátých let minulého století Horacem Dallem a Alanem Kirkhamem. Jeho optické prvky jsou snadno vyrobitelné a měřitelné. Tyto dalekohledy lze vybavit korektory a vytvořit z nich víceúčelové přístroje jak pro planetární pozorování, tak pro fotografování širokých zorných polí. Několik takových přístrojů bylo vyrobeno i v dílně Centra Toptec v Turnově. The paper deals with the optical aberrations of the two-mirror telescopes composed of the ellipsoidal primary and the spherical secondary mirrors. The system was discovered by Horace Dall and Alan Kirkham at the end of the Twenties of the 20th Century. Its optical elements are easy to manufacture and measure. These telescopes can be equipped by lens correctors and turned into multipurpose devices both for planetary observation and wide field photography. Several telescopes were manufactured in workshop of the Toptec Center in Turnov. Klíčová slova: Two-mirror telescope; field corrector; optical aberrations; spherochromatic aberration; koma; astigmatism Plné texty jsou dostupné na jednotlivých ústavech Akademie věd ČR.
Dalekohledy typu Dall-Kirkham

Referát se zabývá optickými vadami dvojzrcadlových dalekohledů s elipsoidálními primárními a sférickými sekundárními zrcadly. Systém byl objeven na konci dvacátých let minulého století Horacem Dallem ...

Rail, Zdeněk; Ulrichová, Iva; Kuryshev, V.; Vápenka, David
Ústav fyziky plazmatu, 2018

Optický prvek 2G20 6x8x mm
Pintr, Pavel
2018 - český
Optický prvek 2G20 6x8 mm je určen pro proměnné dopravní značení (PDZ) v dopravě. Zajišťuje promíchání RGB diod na bílé světlo a jeho usměrnění do směru dle normy ČSN EN 12966 třídy B6. Optical element 2G20 6x8 mm is designed for a variable traffic marking. It assures the mixing of RGB diodes in white light and its direction in accordance with the specification ČSN EN 12966 class B6. Klíčová slova: optical element; 2G20 6x8 mm; PDZ Plné texty jsou dostupné na jednotlivých ústavech Akademie věd ČR.
Optický prvek 2G20 6x8x mm

Optický prvek 2G20 6x8 mm je určen pro proměnné dopravní značení (PDZ) v dopravě. Zajišťuje promíchání RGB diod na bílé světlo a jeho usměrnění do směru dle normy ČSN EN 12966 třídy B6....

Pintr, Pavel
Ústav fyziky plazmatu, 2018

The role of microstructure on wettability of plasma sprayed yttria stabilized zirconia coatings
Komarov, P.; Čelko, L.; Remešová, M.; Skorokhod, K.; Jech, D.; Klakurková, L.; Slámečka, K.; Mušálek, Radek
2018 - anglický
Atmospheric plasma spraying utilizing initial powder materials in micrometric size has been successfully used for various applications in different fields of the industry over the past several decades. Nowadays, the new trend in plasma spraying is to use sub-micron or nano-sized powder feedstocks in the form of colloidal suspension. This relatively new technology enables to obtain specific types of dense vertically cracked, fully dense or columnar microstructure. The aim of this work is to investigate the influence of coatings microstructure and topography on its water wetting properties. Two different microstructures, i.e. lamellar and columnar, were sprayed from chemically the same yttria-stabillized zirconia (YSZ) ceramics powders by the means of conventional atmospheric plasma spray and suspension hybrid water stabilized plasma spray techniques, respectively. Microstructural and phase composition of the initial powders and as-sprayed coatings were investigated using optical microscopy, scanning electron microscopy and X-ray diffraction techniques. Topography of coatings surface was measured by means of non-contact optical profilometry. The YSZ coatings wettability was evaluated based on water droplet contact angle using Sessile droplet method. The coatings microstructure reveals the important role in the change of droplet contact angle, where lamellar microstructure was found close to hydrophilic-hydrophobic transition and columnar microstructure was found superhydrophobic Klíčová slova: Contact angle; Plasma spraying; Sessile drop method; Water; Yttria stabilized zirconia Plné texty jsou dostupné na jednotlivých ústavech Akademie věd ČR.
The role of microstructure on wettability of plasma sprayed yttria stabilized zirconia coatings

Atmospheric plasma spraying utilizing initial powder materials in micrometric size has been successfully used for various applications in different fields of the industry over the past several ...

Komarov, P.; Čelko, L.; Remešová, M.; Skorokhod, K.; Jech, D.; Klakurková, L.; Slámečka, K.; Mušálek, Radek
Ústav fyziky plazmatu, 2018

Combined coatings against mechanical wear and corrosion low carbon steel
Brožek, Vlastimil; Pokorný, P.; Kolísko, J.; Vokáč, M.; Mastný, L.; Stoulil, J.
2018 - anglický
In this study, special ceramic coatings were prepared on low carbon steel (1.0060 - EN 10027-2) via the plasma spraying technique using a WSP®-H plasma generator with output of up to 40 kg/h of aluminum oxide. Corundum coatings were deposited directly on the surface of steel plungers equipped with an anti-corrosion interlayer of zinc phosphate. Coating adhesion properties were tested using pin-off tests (modified ISO 4624) and reached a maximum value of 26 MPa. Corrosion resistance was evaluated by measurements of impedance spectra in the 100 kHz - 10 mHz range in a water solution of sodium sulfate. The capacity of electric double-layer varied depending on the porosity and thickness of the coating. Low-porosity coatings of >1.5 mm thickness had RCT 1.29·105 Ω·m2. The abrasive resistance of coatings was measured by rotary/machining test with SiC cutting knives, using a downforce of 50 kg·cm-2. Abrasion losses decreased with the quality of finish - starting at 0.00266 g cm-2 min-1 down to virtually zero losses after polishing the surface below Ra = 0.55 micro m. Klíčová slova: Abrasion; Ceramic coatings; Corrosion resistance; Plasma spraying; Steel phosphating Plné texty jsou dostupné na jednotlivých ústavech Akademie věd ČR.
Combined coatings against mechanical wear and corrosion low carbon steel

In this study, special ceramic coatings were prepared on low carbon steel (1.0060 - EN 10027-2) via the plasma spraying technique using a WSP®-H plasma generator with output of up to 40 kg/h of ...

Brožek, Vlastimil; Pokorný, P.; Kolísko, J.; Vokáč, M.; Mastný, L.; Stoulil, J.
Ústav fyziky plazmatu, 2018

Suspension plasma spraying of sub-stoichiometric titania by hybrid water/argon stabilized plasma torch
Mušálek, Radek; Ctibor, Pavel; Medřický, Jan; Tesař, Tomáš; Kotlan, Jiří; Lukáč, František
2018 - anglický
In this study, suspension plasma spraying of sub-stoichiometric titania was attempted using hybrid water/argon stabilized plasma torch (WSP-H). Porous coatings with fine cauliflower-like columnar microstructure were successfully deposited in two separate experiments with different power levels of the plasma torch. In both cases, high solid-load content (40 wt. %) of the water-based suspension resulted in considerable coating thickness increase per deposition cycle. Coating annealing and partial remelting of the surface asperities were also achieved by additional pass of plasma torch in front of the coating surface. According to X-ray diffraction, all coatings consisted dominantly of rutile phase. Detailed microscopic observation of the as-sprayed and annealed deposits showed that the local coloration of the coating (ranging from dark blue to beige) was driven by the local overheating of the rough coating surface which could also promote the oxygen intake. Moreover, sample annealing was also observed to increase the sample reflectivity as observed by UV-VIS-NIR scanning spectrophotometry Klíčová slova: Liquid feedstock; Plasma spraying; Suspension; Thermal spraying; Titania; WSP-H Plné texty jsou dostupné na jednotlivých ústavech Akademie věd ČR.
Suspension plasma spraying of sub-stoichiometric titania by hybrid water/argon stabilized plasma torch

In this study, suspension plasma spraying of sub-stoichiometric titania was attempted using hybrid water/argon stabilized plasma torch (WSP-H). Porous coatings with fine cauliflower-like columnar ...

Mušálek, Radek; Ctibor, Pavel; Medřický, Jan; Tesař, Tomáš; Kotlan, Jiří; Lukáč, František
Ústav fyziky plazmatu, 2018

Alternative Methods of Permeation Barriers Preparation
Veverka, Jakub; Matějíček, Jiří
2018 - anglický
Permeation barriers represent one of the crucial fields in materials development for thermonuclear fusion. Primary objective of the barriers is to suppress the permeation of hydrogen isotopes (mainly tritium) from future thermonuclear fusion facilities. Secondary objective is to reduce their retention in structural materials. Expected reactor conditions put high demands on the material, as well as on the final barrier quality. Key properties are tritium permeation reduction, absence of defects (especially cracks), high-temperature stability and corrossion resistance, and compatibility with structural materials (mostly ferritic-martensitic steels). Thin nitride layers, identified as promising permeation barriers, were prepared by diffusion-based nitridation and physical vapour deposition (PVD), and characterized. Klíčová slova: Permeation barriers; Nitride layers; PVD coating; Permeation measurement Plné texty jsou dostupné na jednotlivých ústavech Akademie věd ČR.
Alternative Methods of Permeation Barriers Preparation

Permeation barriers represent one of the crucial fields in materials development for thermonuclear fusion. Primary objective of the barriers is to suppress the permeation of hydrogen isotopes (mainly ...

Veverka, Jakub; Matějíček, Jiří
Ústav fyziky plazmatu, 2018

Oprava objektivu 160/2500 turnovské hvězdárny
Rail, Zdeněk; Melich, Zbyněk; Šrajer, Bohdan; Šípová, Gabriela; Kaucká, Iva; Franců, Helena; Melich, Radek
2018 - český
Tento referát přináší informace o opravě achromatického objektivu o průměru 160 mm a ohniskové vzdálenosti 2500 mm, vyrobeného v 70. letech ve Vývojové optické dílně ČSAV v Turnově. Refraktor s tímto dubletem se stal hlavním přístrojem místní hvězdárny. Spojka tohoto objektivu obsahovala šlíry a bylo ji nutné vyrobit novou This paper brings the information about repair of the achromatic objective lens of diameter 160mm and focal length 2500mm produced by the Development Optical Workshop of the ČSAV in Turnov. The refractor with this dublet has become the main telescope of a local astronomical observatory. The positive lens contained impurities – schlieren and it was necessary to produce a new lens and change it. Klíčová slova: Achromatic dublet; aplanat; grinding; polishing; autocollimation test; optical aberrations Plné texty jsou dostupné na jednotlivých ústavech Akademie věd ČR.
Oprava objektivu 160/2500 turnovské hvězdárny

Tento referát přináší informace o opravě achromatického objektivu o průměru 160 mm a ohniskové vzdálenosti 2500 mm, vyrobeného v 70. letech ve Vývojové optické dílně ČSAV v Turnově. Refraktor s tímto ...

Rail, Zdeněk; Melich, Zbyněk; Šrajer, Bohdan; Šípová, Gabriela; Kaucká, Iva; Franců, Helena; Melich, Radek
Ústav fyziky plazmatu, 2018

Tmelený objektiv Steinheilova typu
Rail, Zdeněk; Franců, Helena; Ulrichová, Iva; Šípová, Gabriela; Jareš, Daniel; Kuryshev, V.; Vápenka, David
2018 - český
Tento referát se zabývá achromatickými dublety se vstupním členem z flintového skla. Optické řešení těchto objektivů navrhl německý fyzik Carl August Steinheil v polovině 19. století. V nedávné minulosti bylo několik těchto dubletů vyrobeno pro astronomické účely v naší dílně. V referátu popisujeme výpočet a technologický postup výroby tmeleného Steinheilova objektivu s rovinnou výstupní plochou. This paper analyses the achromatic dublets with an entrance lens of the flint glass. The objective lens of this construction were devised by German physician Carl August Steinheil in the half of the 19 th century. Several pieces of these dublets were manufactured for astronomical purposes in our workshop in the past. We discuse the mathematical evaluation and the method of manufacture of the glued Steinheil objective with plane exit surface. Klíčová slova: Achromatic objective; apochromatic objective; spherochromatic aberration; coma Plné texty jsou dostupné na jednotlivých ústavech Akademie věd ČR.
Tmelený objektiv Steinheilova typu

Tento referát se zabývá achromatickými dublety se vstupním členem z flintového skla. Optické řešení těchto objektivů navrhl německý fyzik Carl August Steinheil v polovině 19. století. V nedávné ...

Rail, Zdeněk; Franců, Helena; Ulrichová, Iva; Šípová, Gabriela; Jareš, Daniel; Kuryshev, V.; Vápenka, David
Ústav fyziky plazmatu, 2018

O službě

NUŠL poskytuje centrální přístup k informacím o šedé literatuře vznikající v ČR v oblastech vědy, výzkumu a vzdělávání. Více informací o šedé literatuře a NUŠL najdete na webu služby.

Vaše náměty a připomínky posílejte na email nusl@techlib.cz

Provozovatel

http://www.techlib.cz

Facebook

Zahraniční báze