Název: Degradation of protective effect of surface layer on Ni3Al-Cr in hydrogen environment
Autoři: Čermák, Jiří ; Rothová, Věra
Typ dokumentu: Příspěvky z konference
Konference/Akce: Materials Structure and Micromechanics of Fracture /3./, Brno (CZ), 2001-06-27 / 2001-06-29
Rok: 2001
Jazyk: eng
Abstrakt: Protective effect of surface layer on Cr-doped (4 and 8 at. % Cr) Ni3Al intermetallic was studied by high-temperature hydrogen permeation tests that were carried out at temperatures in the interval 775-1223 K. Hydrogen with about 1 vol. ppm O2 and 2 vol. ppm of H2O was used for the gas-permeation tests. It was observed that the addition of Cr degrades the - otherwise very good - high-temperature protective ability of oxide-containing surface layer of Ni3Al-Cr at strongly reducing hydrogen environment.
Klíčová slova: hydrogen; intermetallics; surface
Číslo projektu: CEZ:AV0Z2041904 (CEP), IBS2041105 (CEP), GA106/99/1179 (CEP)
Poskytovatel projektu: GA AV ČR, GA ČR
Zdrojový dokument: Materials Structure and Micromechanics of Fracture

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0074681

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-26500


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference