Název: Fatigue properties of nickel-base superalloy inconel 792-5A at 800°C
Autoři: Šmíd, Miroslav ; Obrtlík, Karel ; Petrenec, Martin ; Polák, Jaroslav ; Hrbáček, K.
Typ dokumentu: Příspěvky z konference
Konference/Akce: Metal 2010. International Conference on Metallurgy and Materials /19./, Rožnov pod Radhoštěm (CZ), 2010-05-18 / 2010-05-20
Rok: 2010
Jazyk: eng
Abstrakt: Smooth specimens were cyclically strained under strain control with constant strain amplitude and constant strain rate. Low cycle fatigue tests were conducted in servo-hydraulic pulsator MTS equipped with a three zone resistance furnace at temperature 800°C in air. Fracture surface was studied in SEM after fatigue test termination. Selected specimens were used to prepare foils for the transmission electron microscope (TEM) observation of microstructure and dislocation arrangement. They were used to obtain cyclic hardening/softening curves, cyclic stress-strain curve and fatigue life curves in the representation of stress amplitude, total strain amplitude and plastic strain amplitude versus number of cycles to fracture. Experimental points can be approximated with the Manson-Coffin law and the Basquin law. Fracture surface examinations revealed fatigue crack initiation sites.
Klíčová slova: dislocation structure; fatigue life curves; high temperatures; Inconel 792-5A; low cycle fatigue
Číslo projektu: CEZ:AV0Z20410507 (CEP), GA106/08/1631 (CEP)
Poskytovatel projektu: GA ČR
Zdrojový dokument: Metal 2010 - 19th international conference on metallurgy and materials, ISBN 978-80-87294-15-4

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0193237

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-42387


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference