Název: Fatigue strength of wheathering steel ATMOFIX 52A
Autoři: Kunz, Ludvík ; Vlk, M. ; Zavadilová, Petra ; Klusák, Jan ; Navrátilová, L.
Typ dokumentu: Příspěvky z konference
Konference/Akce: Applied Mechanics 2011, Velké Bílovice (CZ), 2011-04-18 / 2011-04-20
Rok: 2011
Jazyk: eng
Abstrakt: Deterioration of fatigue properties of weathering steels is a serious problem of operating life of engineering components subjected to corrosion and cyclic loads. There are two possible mechanisms of damage, which are discussed in literature. There is an effect of surface roughening, which develops during corrosion, and an effect of corrosion cracks, which can influence the fatigue crack initiation. The paper contains results of an experimental determination of fatigue life of ATMOFIX 52A grade steel with a corroded surface and comparison with the fatigue strength of basic smooth material. The notch effect of corrosion dimples, which initiated fatigue cracks, was determined on the basis of fractographic observation and numerical evaluation of stress concentration. It has been found that the reduction of the fatigue life can be quantitatively well predicted by means of the fatigue notch effect of corrosion dimples. No risky corrosion cracks were found in the studied corroded material
Klíčová slova: ATMOFIX; fatigue; weathering steel
Číslo projektu: CEZ:AV0Z20410507 (CEP)
Zdrojový dokument: Applied Mechanics 2011 - Conference Proceedings, ISBN 978-80-87434-03-1

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0206669

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-85973


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference